Preparation and Characterization of Multielement Composite Oxide Nanomaterials Containing Ce, Zr, Y, and Yb via Continuous Hydrothermal Flow Synthesis

The synthesis of multielement composite oxide nanomaterials containing Ce, Zr, Y, and Yb was investigated using a micro confined jet mixer reactor operated in continuous mode under supercritical water conditions. The obtained nanoparticles were characterized using ICP-AES, SEM-EDS, FTIR, Raman spectroscopy, XRD, and TEM. All samples exhibited a uniform particle shape and a narrow particle size distribution. An analysis of the d-spacing results using selected electron area diffraction (SAED) patterns confirmed the production of cubic-phase crystals. A BET test was employed to determine the specific surface area of the prepared nanoparticles. OSC and TPR techniques were utilized to characterize the oxygen storage capacity and reduction performance of the obtained samples, with an analysis conducted to determine how the different proportions of elements affected the performance of multielement mixed oxides. The ionic conductivity of multielement composite oxide was measured using alternating current impedance spectroscopy (EIS), and the impact of Y, Ce, and Yb on the electrolyte material’s ionic conductivity was analyzed.